| Customization: | Available |
|---|---|
| Application: | Tech Industry |
| Purity: | >99.99% |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Exquisite Quality Pure Metal Ingots: Discover our premium selection of 99.994% pure lead ingots, aluminum alloy, zinc ingot, and tin ingot, all offered at competitive prices by a trusted manufacturer.
1. Perfect for the die-casting alloy and battery industries, our zinc ingots offer supreme quality and reliability.
2. Extensively utilized across various sectors including painting, printing, dyeing, pharmaceutical, and rubber industries, ensuring versatility and adaptability.
3. Widely applied in the chemical industries, and metal alloy plating and coating sectors, our zinc ingots are essential for numerous industrial applications.
4. Our zinc ingots play a critical role in zinc plating, brass manufacture, manganese bronze, and galvanized iron production. They are also valued as catalysts and reducing agents.
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |