| Customization: | Available |
|---|---|
| Application: | Tech Industry |
| Purity: | >99.99% |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Pure Metal 99.994%: Immerse yourself in the exceptional purity of our lead, aluminum alloy, zinc, and tin ingots, proudly presenting a purity level of 99.994%. Our dedication to providing affordable solutions without sacrificing quality makes us a top-tier choice for manufacturers who require superior metal products at a reasonable cost.
1. This versatile product is predominantly employed in the die-casting alloy and battery industries, delivering unmatched quality and superior performance that sets the benchmark in its category.
2. With its exceptional quality and adaptability, it is widely applied across diverse sectors, including painting, printing, dyeing, pharmaceuticals, and rubber, showcasing its versatile utility.
3. Within the chemical industry, it plays vital roles in zinc and metal alloy plating and coating processes, guaranteeing premium finishes and enhanced durability.
4. Indispensable in zinc plating, brass manufacturing, manganese bronze production, and galvanizing iron, as well as dry battery production, it also acts as a highly effective catalyst and reducing agent, highlighting its multifaceted capabilities.
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |