| Customization: | Available |
|---|---|
| Application: | Tech Industry |
| Purity: | >99.99% |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Pure Metal 99.994%: Unlock the exceptional world of our top-tier lead ingots, aluminum alloy, zinc ingots, and tin ingots with an awe-inspiring purity of 99.994%. Our meticulous attention to quality allows us to offer these superior metal solutions at competitive prices, ensuring that manufacturers gain access to the finest materials without compromising on cost-efficiency. Experience the perfect blend of affordability and excellence with Shandong Yien, your ultimate partner in premium metal procurement.
1. This versatile marvel finds its primary application in the die-casting alloy and battery industry, delivering unparalleled quality and exceptional performance. Witness its transformative impact across these sectors.
2. Its remarkable versatility finds it an indispensable resource across sectors like painting, printing, dyeing, pharmaceuticals, rubber, and more. Revel in its superior quality and unmatched adaptability.
3. In the chemical industry, it plays vital roles in zinc and metal alloy plating and coating processes. Expect high-quality finishes and exceptional durability, elevating standards in industrial applications.
4. An essential component in zinc plating, brass manufacturing, manganese bronze production, galvanizing iron, and dry battery production, it also shines as an efficient catalyst and reducing agent, demonstrating its multifaceted utility and importance across various applications.
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |