| Customization: | Available |
|---|---|
| Application: | Tech Industry |
| Purity: | >99.99% |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Pure Metal 99.994%: Unlock the premium standard of our range of ingots including lead, aluminum alloy, zinc, and tin. Our steadfast promise to deliver exceptional value without compromising on quality positions us as the top choice for manufacturers who prioritize both cost-effectiveness and superior metal solutions.
1. This versatile product is predominantly used in the die-casting alloy and battery sectors, delivering unmatched quality and exceptional performance.
2. It serves a wide range of applications across various industries including painting, printing, dyeing, pharmaceuticals, rubber, and more, due to its outstanding quality and adaptability.
3. In the chemical industry, it plays vital roles in zinc and other metal alloy plating and coating processes, ensuring superior finishes and longevity.
4. Integral to zinc plating, brass manufacturing, manganese bronze production, galvanizing iron, and dry battery production, it functions as an effective catalyst and reducing agent, highlighting its versatile applications.
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |
){kind=link}