| Customization: | Available |
|---|---|
| Application: | Tech Industry |
| Purity: | >99.99% |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Pure Metal 99.994% Lead Ingots Aluminum Alloy Zinc Ingot Tin Ingot With Cheap Price Manufacturer
1. Primarily utilized in the die-casting alloy battery industry, offering exceptional quality and performance.
2. Extensively applied in a myriad of industries, including painting, printing, dyeing, pharmaceuticals, and rubber, showcasing its versatility.
3. A key player in chemical industries, our zinc ingot is integral to zinc and other metal alloy plating and coating applications.
4. Essential in zinc plating, the manufacture of brass and manganese bronze, galvanizing iron, and dry batteries. Additionally, it serves as a catalyst and reducing agent.
Brand |
Chemical | |||||||||
| Zn(≥) | Impurity(≤) | |||||||||
| Pb | Cd | Fe | Cu | Sn | Al | As | Sb | Totsal | ||
| Zn99.995 | 99.995 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.001 | -- | -- | 0.005 |
| Zn99.99 | 99.99 | 0.005 | 0.003 | 0.003 | 0.002 | 0.001 | 0.002 | -- | -- | 0.01 |
| Zn99.95 | 99.95 | 0.03 | 0.01 | 0.02 | 0.002 | 0.001 | 0.01 | -- | -- | 0.05 |
| Zn99.5 | 99.5 | 0.45 | 0.01 | 0.05 | -- | -- | -- | 0.005 | 0.01 | 0.5 |
| Zn98.5 | 98.5 | 1.4 | 0.01 | 0.05 | -- | -- | -- | -- | -- | 1.5 |
| ltimate tensile strength | 331 MPa (270 MPa aged) | 48,000 psi (39,000 psi aged) |
| Yield strength (0.2% offset) | 295 MPa | 43,000 psi |
| Impact strength | 52 J (56 J aged) | 38 ft-lbf (41 ft-lbf aged) |
| Elongation at F max | 2% | |
| Elongation at fracture | 3.6% (13% aged) | |
| Shear strength | 262 MPa | 38,000 psi |
| Compressive yield strength | 600 MPa | 87,000 psi |
| Fatigue strength (reverse bending 5x10 8 cycles) | 57 MPa | 8,300 psi |
| Hardness | 114 Brinell | |
| Modulus of elasticity | 96 GPa | 14,000,000 psi |
| Solidification range (melting range) | 380386 °C | 716727 °F |
| Density | 6.7 kg/dm 3 | 0.24 lb/in 3 |
| Coefficient of thermal expansion | 27.4 μm/m-°C | 15.2 μin/in-°F |
| Thermal conductivity | 109 W/mK | 756 BTU-in/hr-ft 2 -°F |
| Electrical resistivity | 6.54 μΩ-cm at 20 °C | 2.57 μΩ-in at 68 °F |
| Latent heat (heat of fusion) | 110 J/g | 4.7x10 -5 BTU/lb |
| Specific heat capacity | 419 J/kg-°C | 0.100 BTU/lb-°F |
| Coefficient of friction | 0.08 | |
){kind=link}